Magnesia-Carbon Bricks For EAF Name:Magnesia-Carbon Bricks Chemical CompositionApparent Porosity %Bulk Density g/cm3Cold Crushing Strength MpaMgOCMT-88484.53.0245MT-10821043.0040MT
Converter Magnesia-carbon Brick Name:Converter Magnesia-carbon Brick Converter Magnesia-Carbon Brick- Such brick is made through high-pressure forming, with high energy electrofused
Alumina-Magnesia-Carbon Bricks Name: Alumina-Magnesia-Carbon Bricks chemical composition(%)A.P.( %)Bulk Density ,g/cm3Cold Crushing Strength, MpaMgOCAl2O3AMC - 659 min8 min65 min8.
Magnesia-Carbon Bricks Name: Magnesia-Carbon Bricks Chemical CompositionApparent Porosity %Bulk Density g/cm3Cold Crushing Strength MpaMgOCMT-1082104.003.0245MT-1280123.503
Brown Fused Alumina Name:Brown Fused Alumina Cargo:Brown Fused AluminaSpecifications as follows:Al2O395% minSiO21.5% maxFe2O30.5% maxTiO23.2% maxK2O+Na2O0.25% maxCaO+MgO
Auminate Cement CA-50-G6 Name:Auminate Cement CA-50-G6 60Aluminate Cement manufactured by sintered method in rotary kiln are according with up-to-date standard GB201-2000,whi
High Alumina Cement Name : High Alumina Cement CA50CA·50-G9(GB201-2000)Chemical compositionAl2O3%50,60 55SiO28.06.0Fe2O32.52.5R2O0.40.4S(0.1)*-Cl(0.1)-Physical pr
Fused calcium alumina Name:Fused calcium alumina Quality & Type type Chemical composition% CaO Al2O3 SiO2 TiO2 Fe2O3 MgO CaF2 BaO DFS-5 48 52 38 42 3 5 2.0 1.5 1.5
Sintered calcium alumina Name:Fused calcium alumina Quality & Type type Chemical composition% CaO Al2O3 SiO2 TiO2 Fe2O3 MgO CaF2 BaO DFS-5 48 52 38 42 3 5 2.0 1.5 1.5
Calcined Kaolin Name: Calcined KaolinKaolin have good whiteness about 75-80%, high bulk density, fewer impurities, physical and stable chemical properties, high temp
Rotary Kiln Bauxite and Round Kiln Bauxite Name:Rotary Kiln Bauxite, Round Kiln Bauxite and Shaft Kiln Bauxite CargoSpecificationsPackingAl2O3SiO2TiO2Fe2O3K2O+Na2OCaO+MgOB.D.Size/Size distribu
Tundish Coating Name:Tundish Coating Main Properties IndexItemTNGZ-1TNGZ-2TNGZ-3chemical moisture , %MgO807580CaO ---46Fe2O3---34bulk density, g/cm3 ≥1200°C2.
Self-flow Castable material Name:Self-flow Castable Main Properties IndexItemTN-SF-3TN-SF3Gchemical moisture , % ≥Al2O3 + MgO90---Al2O3 + MgO + Cr2O3---90bulk density, g/cm3
Ladle Castable material Name:Ladle Castable Main Properties IndexItemLMJ-75ALMJ-75BLMJ-75CLMJ-85ALMS-85BLMS-85CLMS-85DAl2O3 +MgO, % ≥848688848587902.802.852.902.82.93.03.
Drainage Sand Name:Drainage Sand Main PropertiesIndexItemTN-YL-1TN-YL-2TN-YL-3chemical moisture , % ≥SiO2934635MgO---25---Cr2O3------24C2---2refractoriness , &d